A eutectic composition .46.5% CaO–53.5% Al O calcium aluminate fiber formed by Inviscid Melt Spinning .IMS 23 was analyzed using micro-Raman spectroscopy. The fiber surface was shown to consist of pyrolytic graphite. Analysis along the fiber cross-section showed that the pyrolytic graphite layer had a total thickness of approximately 15 mm. Micro-Raman analysis of the fiber bulk was consistent with amorphous calcium aluminate .CaAl O . q2000 Elsevier Science B.V. All 24 rights reserved.
A eutectic composition .46.5% CaO–53.5% Al O calcium aluminate fiber formed by Inviscid Melt Spinning .IMS 23 was analyzed using micro-Raman spectroscopy. The fiber surface was shown to consist of pyrolytic graphite. Analysis along the fiber cross-section showed that the pyrolytic graphite layer had a total thickness of approximately 15 mm. Micro-Raman analysis of the fiber bulk was consistent with amorphous calcium aluminate .CaAl O . q2000 Elsevier Science B.V. All 24 rights reserved.
由非粘性熔融纺丝ims23形成的共晶成分46.5% CaO–53.5% Al O铝酸钙纤维是用微型拉曼光谱分析得来的.纤维表面显示出它是由高温分解石墨组成的.纤维交叉的地方表现出热解石墨层有总共15mm厚.微拉曼光谱分析出纤维体积由不定型铝酸钙CaAl O组成.q2000艾斯维尔公司保留所有24种权利.